PA6 GF15 with high tensile strength is made by 15% glass fiber reinforced, toughened, polyamide 6 resin for injection molding.

Typical Application of PA6 GF15 with high tensile strength (A1307C)

PA6 with 15% glass fiber toughened plastics, due to its excellent properties, good appearance and easy processing characteristics, which has been successfully applied to the electrical field such as switches, controllers, the auto field such as heat dissipation barriers, accumulator shells, coolant pots, and the mechanical filed such as electric drill and motor housing, pump impeller, pulley, tool handle and bearing.

Processing Detail of PA6 GF15 with high tensile strength (A1307C)

Other Details of PA6 GF15 with high tensile strength (A1307C)

Physical Property

Ash                     (15.0% 1 ISO3451/1)

Conditioned 600°C*2h

Density (1180Kg/m3 1 ISO1183)

Conditioned 23°C

Shrinkage Parallel Flow (0.5-0.7 % 1 ISO294-4)

Shrinkage Vertical Flow (0.7-1.1% I ISO294-4)

Mechanical Properties

Tensile strength (115.0MPa 1 ISO527)

Conditioned 5mm/ min

Tensile Strain at Break (2.0% I ISO527)

Conditioned 1.0J

Notched Impact Strength (125 0MPa I ISO527)

Conditioned 2mm/min

Flexural Strength (175MPa 1ISO178)

Conditioned 2mm/min

Flexural Modulus (5250 MPa I ISO178)

Conditioned 5mm/ min

Thermal Property

Melting Point (220°C I ISO11357)

Hot Deformation Temperature (175*C I ISO75)

Conditioned 1.8MPa

Flammability Class (HB 1UL94)

Conditioned mm

Injection Molding Conditions

Drying Temperature 130°C

Drying Time 3h

Cylinder Temperature 240-260°C

Nozzle Temperature 240-260*C

Tooling Temperature 80*C

* Molding conditions are just for reference, please make an adjustment based on the actual situation！

Want to buy masterbatch, contact us.