PA6 6GF15 is a 15% glass fiber reinforced, toughened, polyamide 66 resin for injection molding

Typical Application of Anmei Group PA66 GF15 With High Tensile Strength (A2307C)

PA66 15% glass fiber and high toughness modified grades are applied to the sectors of electrical switch with high tensile characteristics.

Processing Detail of PA66GF15 With High Tensile Strength (A2307C)

Other Details of PA66 GF15 With High Tensile Strength (A2307C)

Physical Property

Ash (15.0% 1 ISO3451/1)

Conditioned 600°C*2h

Density (1180Kg/m3 1 ISO1183)

Conditioned 23°C

Shrinkage Parallel Flow (0.7-1.0 % 1 ISO294-4)

Shrinkage Vertical Flow (1.0-1.4% I ISO294-4)

Mechanical Properties

Tensile strength (105.0MPa 1 ISO527)

Conditioned 5mm/ min

Tensile Strain at Break (2.6% I ISO527)

Conditioned 5mm/ min

Notched Impact Strength (10.0 KJ/m2 I ISO179)

Conditioned 1.0J

Flexural Strength (177MPa 1ISO178)

Conditioned 2mm/min

Flexural Modulus (5050 MPa I ISO178)

Conditioned 2mm/min

Thermal Property

Melting Point (260°C I ISO11357)

Hot Deformation Temperature (225*C I ISO75)

Conditioned 1.8MPa

Flammability Class (HB 1UL94)

Conditioned mm

Injection Molding Conditions

Drying Temperature 130°C

Drying Time 3h

Cylinder Temperature 280-300°C

Nozzle Temperature 280-300*C

Tooling Temperature 80-100*C

* Molding conditions are just for reference, please make an adjustment based on the actual situation！

If you want to know more about pa66 gf15 material properties, please visit our website.